Mirror Hairline Finish Stainless Steel Sheet Plate 405 409 416 420j2

Place of Origin Jiangsu, China
Certification ISO9001, CE
Minimum Order Quantity 1 pcs
Delivery Time 7~10working days
Payment Terms L/C, T/T
Supply Ability 5000 Ton/Tons per Month
Product Details
Product Name Stainless Steel Sheet Type Cold Rolled,Hot Rolled
Surface No.1,2D,2B,BA,No.4,8k,Tempered Thickness 0.4mm~6mm
High Light

405 stainless steel plate

,

409 stainless steel plate

,

416 stainless steel plate

Leave a Message
Product Description

Grade 304 Stainless Steel Sheet

304(1.4301)/304L(1.4307)/304H(1.4948) STAINLESS STEEL

 

Stainless Steel Grade 304 is the standard 18/8 (18% chrome, 8% nickel) austenitic stainless steel. It is a non-magnetic alloy in the annealed condition, however, becomes magnetic as it is cold worked. It is the most ordinarily utilized of all stainless grades. T304 can be effortlessly welded and is the preferred for many deep drawn, spun or formed parts due to its high ductility.

 

Stainless Steel Grade 304L has oxidation resistance to a maximum temperature of 1650°F (899°C) continuous without considerable scaling. The maximum temperature for intermittent presentation is 1500°F (816°C). Since 304L is an additional low-carbon variety of 304 it can frequently be utilized in the “as-welded” condition (without annealing), even in severe corrosive conditions, except for applications indicating stress relief. 304L has good welding qualities and can be welded by all standard strategy; however, consideration should be paid to maintain a strategic distance from weld “hot cracking”. To relieve stress during severe forming or spinning welding may be followed by annealing.

 

Stainless Steel Grade 304H includes a high carbon content making the steel more suitable for utilization in applications where high temperatures are available. The benefit of this grade is that it is an austenitic chromium-nickel steel alloy as well as the greater carbon content distribute to increased tensile and yield strength. The material is recommended for utilizing in ASME pressure vessels in working service above 525° C because of the grade's heat resistant properties.

 

CHEMICAL COMPOSITION

Element C Mn Si P S Cr Ni Fe
302 0.15% 2.0% 0.75% 0.045% 0.03% 17.0~19.0% 8.0~10.0% Remainder
303 0.10% 2.0% 1.00% 0.040% 0.015% 17.0~19.0% 8.0~10.0% Remainder
304 0.07% 2.0% 0.75% 0.045% 0.03% 17.5~19.5% 8.0~10.5% Remainder
304L 0.03% 2.0% 0.75% 0.045% 0.03% 17.5~19.5% 8.0~12.0% Remainder
304H 0.04~0.10% 2.0% 0.75% 0.045% 0.03% 18.0~20.0% 8.0~10.5% Remainder
309 0.20% 2.0% 0.75% 0.045% 0.03% 22.0~24.0% 12.0~15.0% Remainder
321 0.08% 2.0% 0.75% 0.045% 0.03% 17.0~19.0% 9.0~12.0% Remainder
330 0.08% 2.0% 0.75~1.50% 0.03% 0.03% 17.0~20.0% 34.0~37.0% Remainder
347 0.08% 2.0% 0.75% 0.045% 0.03% 17.0~19.0% 9.0~13.0% Remainder

 

MECHANICAL PROPERTIES

Grade

 

Tensile Strength

(MPa)

Min

 

 

Yield Strength

0.2% Proof

(MPa)

Min

 

Elongation

(%in 50mm)

Min

Hardness

Rockwell B

(HR B)

Max

Brinell

(HB)

Max

302 620 275   85 147
303 620 310 30 96 230
304 515 205 40 92 201
304L 485 170 40 92 201
304H 515 205 40 92 201
309 515 205 40 95 217
321 515 205 40 95 217
330 552 207 40 95 217
347 515 205 40 92 201

 

304/304L/304H COMMON APPLICATIONS

  • Air Bag Sensors
  • Clamps
  • Bellows
  • Flexible Hoses
  • Hinges
  • Cryogenic Components
  • Surgical Instruments
  • Pressure Vessels
  • Oil Well Filter Screen
  • Hypodermic Needles
  • Medical Parts
  • Tubing