Low Carbon Steel Bar Rod Aisi 1018 SAE/AISI 1022 1060 Carbon Steel Flat Bar
Product Name | Carbon Steel Flat Bar | Thickness | ≥3mm |
---|---|---|---|
Delivery Condition | Annealing,Normalized,Quench+Temper | Surface | Black Finish,Peeled,Rough Turned |
High Light | 1095 steel flat bar,low carbon steel aisi 1018,low carbon steel rod aisi 1018 |
Mild Steel Flat Bar is a versatile product commonly used in fabrication. With a flat surface and square edge, Sizing is represented as Width x Thickness, for example 40 x 25 = (45 mm Wide x 25mm Thick).
1022 is a general purpose low tensile low hardenability carbon steel generally supplied in the black hot rolled condition, with a typical tensile strength range 360 - 560 Mpa and Brinell hardness range 100 - 170.Characterised by excellent weldability, fairly good machinability with reasonable strength and good ductility.
Product can be purchased in individual lengths or as a bundle and we can also cut to length.
GRADE
AISI |
AISI 1008 AISI 1015 AISI 1017 AISI 1021 AISI 1025 AISI 1026 AISI 1035 AISI 1045 AISI 1050 AISI 1055 |
ASTM |
SAE 1006 SAE 1008 SAE 1010 SAE 1020 SAE 1030 SAE 1030 SAE 1035 SAE 1040 SAE 1045 |
JIS | SCM415 SCM420 SCM440 SS400 S45C S20C |
GB | Q195 Q215 Q235 |
SIZE
Size(mm) | Weight(kg/m) | Length(m) |
10 × 3 | 0.24 | ≥4 |
13 × 3 | 0.31 | ≥4 |
13 × 5 | 0.51 | ≥4 |
13 × 6 | 0.61 | ≥4 |
16 × 3 | 0.38 | ≥4 |
16 × 5 | 0.63 | ≥4 |
... | ... | ... |
EQUIVALENT GRADE OF 1022
BS | Germany DIN | GB | Japan JIS |
EN 3C | CK22 | 22# | S20C |
CHEMICAL COMPOSITION
Element | C | Mn | P | S |
1006 | 0.08% Max | 0.25~0.40% | 0.04%Max | 0.05%Max |
1008 | 0.10%Max | 0.30~0.50% | 0.04%Max | 0.05%Max |
1010 | 0.08~0.13% | 0.30~0.60% | 0.04%Max | 0.05%Max |
1020 | 0.18~0.23% | 0.30~0.60% | 0.04%Max | 0.05%Max |
1022 | 0.16~0.24% | 0.70~1.00% | 0.04%Max | 0.05%Max |
1025 | 0.22~0.28% | 0.30~0.60% | 0.04%Max | 0.05%Max |
1045 | 0.43~0.50% | 0.60~0.90% | 0.04%Max | 0.05%Max |
HEAT TREATMENT
It can be heat treated at the following temperatures:
- Normalizing at 899°C – 954°C (1650°F-1750°F)
- Annealing at 843°C – 871°C (1550°F-1600°F)
- Stress relieving at 677°C – 927°C (1250°F-1700°F)
- Carburizing at 899°C – 927°C (1650°F-1700°F)
- Hardening at 788°C – 816°C (1450°F-1500°F)